Perlite Plaster

LIGHTWEIGHT PLASTER FOR BUILDINGS, B4 (HAND-APPLIED PLASTER) 1. Product Description

Hand-Applied Plaster is a plaster-based interior surface plaster with enhanced heat and insulation properties.

2. Ingredient Information

Calcium Sulfate Hemihydrate+Calcium Carbonate+Calcium Hydroxide+Expanded Perlite+Tartaric Acid+Cellulosic Ether+Sodium Alpha Sulfate

3. Physical and Chemical Properties

Form: Powder
Odor: Odorless
Color: White, yellowish
Solubility in Water: Soluble in water

4. Relevant Standards/Declarations

TS EN 13279-1: Building Plasters and Plastering Compounds - Lightweight plastering compound for buildings (hand-applied plastering compound)

B4/20/2

CE Declaration

5. Application Areas

Concrete
Exposed concrete
Pumice blocks
Applied on brick surfaces.

6. Packaging

Polypropylene laminated bag, 35 ±2%

7. Storage Conditions

Must be stored in its original packaging, closed, in a dry place and on pallets.

8. Advantages

Due to its chemical composition, it does not promote the growth of bacteria, mold, or fungi. It has fire-retardant properties due to the water content in its structure. It is sound-absorbent due to its porous structure. It is a building material with low thermal conductivity. It balances the humidity level of the environment, creating a healthy atmosphere. Its long processing time allows for comfortable and waste-free application.

9. Application Surface Properties

The application environment temperature must be at least +5°C. Substances that prevent adhesion on the application surface (dust, oil, etc.) must be cleaned. Before application, surfaces that are dry, warm, and highly absorbent must be moistened with water. A plaster mesh should be used at the joints of different materials to prevent cracking. The surface of smooth ceilings should be roughened or primed with a material that promotes adhesion of the mortar before plastering. Trowel applications should be thin and single-layer.

10. Preparing the Mortar

Pour the appropriate amount of water into a clean container (water/plaster ratio: 6 liters of water to 10 kg of ALL Perlite Plaster). Sprinkle ALL Hand-Applied Plaster onto the water. Allow the mortar to sit for 1-2 minutes to ensure complete contact and absorption of the water. The mortar is ready for use after mixing. The mortar must be used within 70-80 minutes.

11. Application

Check the smoothness of the surface to be applied and determine the plaster thickness according to the surface smoothness. Anchors suitable for the plaster thickness are placed. The mortar is applied to the surface with a trowel or plastering trowel. Excess mortar is scraped off the surface by smoothing. To obtain a glossy surface, the surface is smoothed with a steel trowel after 45 minutes. Before painting, ALL Fine Applicable Plaster is applied to the surface.

12. Shelf Life

The shelf life is 6 months from the date of manufacture.

13. Technical Specifications

Technical specifications may vary depending on site conditions and substrate characteristics.

TEKNOGİPS TOZ TSE – 24.01.2027

Technical Specifications

1. Physical Appearance	White powder
2. Content	Calcium sulfate Hemihydrate + Calcium Carbonate + Calcium Hydroxide + Expanded Perlite + Cellulose Ether + Tartaric Acid + Sodium Alpha Sulfonate
3. Water/Plaster Ratio	6 liters of water per 10 kg of plaster
4. Setting Start Time (td)	min. 20 min – max. 90 min.
5. Freezing Time (t3)	90–180 min.
6. Bulk Density	-
6.1 Density (K.L.A)	700–800 g/L
7. Spread Diameter	160–170 mm
8. PH	12–13 for a 1 liter measured container
9. Tensile Strength in Bending	TSE YILDIZ PS: ≥1.4 N/mm², TSE PS: ≥1.0 N/mm²
10. Compressive Strength	TSE YILDIZ PS: ≥3.1 N/mm², TSE PS: ≥2.0 N/mm²
11. Adhesion Strength	TSE YILDIZ PS: ≥0.3 N/mm², TSE PS: ≥0.1 N/mm²
12. Fire Reaction	A1
13. Consumption Amount	8.5–9.5 kg/m² (10 mm thickness)
14. Application Thickness	Min. 10 mm – Max. 15 mm
15. Packaging	15.1 Type: Polypropylene Bag 15.2 Net Weight: 35 kg ±2